FeCrAl 0Cr23Al5 Gas Furnace Wire Mesh
The FeCrAl 0Cr23Al5 Gas Furnace Wire Mesh is a ferritic iron-chromium-aluminium alloy (FeCrAl alloy) which is used at temperatures up to 1250°C. It is used in fast response elements for ceramic glass top hobs and quartz tube heaters. FeCrAl 0Cr23Al5 Gas Furnace Wire Mesh is widely used in household lectrical appliance, heating elements, mechanical manufacturing and other industrial fields.
Chemical Composition (%) and Properties
|
H23YU5 0Cr23Al5
|
|
Main Chemical Composition
|
Cr
|
20.5-23.5
|
|
Al
|
4.2-5.3
|
|
Fe
|
Rest
|
|
Mn
|
≤0.7
|
|
Max Continuous Service Temp.of Element °C
|
1250
|
|
Density g/cm³
|
7.25
|
|
Resistivity Ω m²/m
|
1.35±0.06
|
|
Temp.Coefficient of Resistance
|
14.5
|
|
Melting point
|
°C
|
1500
|
|
Tensile strength
|
Mpa
|
637-784
|
|
Elongation %
|
|
>12
|
|
Variation of area
|
%
|
65-75
|
|
Bending frequency
|
|
>5
|
|
Hardness
|
200-260
|
|
Micrographic Structure
|
F
|
|
Magnetic Property
|
|
Magnetic
|
Mesh Specification
The manufacture of mesh is started with producing wire. The wire production includes: forging, rolling, annealing and drawing. The wire with right material and wire diameter will be produced. Then the warp wires will be put and prepared on the weaving machine, and then start weaving. From wire to mesh, manufacture process is operated with high standard quality control system. There will be quality test for each batch of product, such as test to diameter tolerance, content, mesh aperture, etc.
Packing Process & Transportation
Packaging: Seal up, with plastic inside and wooden case or carton outside; or according to the customer's requirements.
Transportation: By air or By sea
Other Terms
|
Minimum Order Quantity
|
Manufacture Period
|
Payment Terms
|
|
100 KG
|
10-15 Days (Small Quantity)
|
20-40 Days (Mass Quantity)
|
L/C, T/T, Western Union
|