NICKEL 201 (N02201) WIRE MESH / SCREEN
Commercially pure wrought Nickel 201 has similar properties to Alloy 200 but with a lower carbon content to prevent embrittlement by inter-granular carbon at elevated temperatures.
Nickel 201 is the low carbon version of Nickel 200. It is preferred to Nickel 200 for applications involving exposure to temperatures above 600°F. With low base hardness and lower work-hardening rate, it is particularly suited for cold forming.
To ensure the quality of our product, we can produce the product with raw materials from the international suppliers. Every batch of product can be tracked to the original raw material supplier. We co-operate with international suppliers like Allvac(ATI), Bohler, Carpenter, Dunkirk, Gloria, OttoKumpu, SMC, ThyssenKrupp VDM, Valbruna, etc.
Chemical Composition(%) of Nickel 201 Wire Mesh:
|
|
Ni |
Mn |
C |
Si |
Fe |
Cu |
S |
|
Max |
|
0.35 |
0.02 |
0.35 |
0.40 |
0.25 |
0.01 |
|
Min |
99.0 |
|
|
|
|
|
|
Physical Properties of Nickel 201 Wire Mesh:
|
Density |
8.9 g/cm3 |
|
Specific Heat |
440 J/kg K |
|
Electrical Resistivity |
8.5 micro ohms cm |
|
Curie Temperature |
358℃ |
|
Melting Range |
1435-1445℃ |
|
Thermal Expansion |
(106K) 14.3 (20-300℃) |
Mechanical Properties of Nickel 201 Wire Mesh:
|
Ultimate Tensile |
≥50KSi (≥345MPa) |
|
Yield Strength (0.2% OS) |
≥10KSi (≥70MPa) |
|
Elong |
≥40 |
Applications of Nickel 201 Wire Mesh:
1. Manufacture and handling of sodium hydroxide, particularly at temperature above 300C.
2. Production of viscose rayon. Manufacture of soap.
3. Alanine hydrochloride production and in the chlorination of aliphatic hydrocarbons such as benzene, methane and ethane.
4. Manufacture of vinyl chloride monomer.
5. Reactors and vessels in which fluorine is generated and reacted with hydrocarbons.
Product Description of Nickel 201 Wire Mesh:
The product produced by us is of good quality and is priced reasonably.
Competitive price: The labour cost and cost on procuring the raw materials is low and hence the manufacturing cost is reasonable. We provide high facility in short producing cycle and have strong adaptive capacity in producing variation of products.
High quality assured: The work done by us has a good command of advanced technological process in the respect of smelting, rolling, drawing and heat treatment up to finished products. The chemical analysis department, the physical testing department and the quality control department all operate an all-round monitoring of our products from raw materials to final products.
Manufacture Process of Nickel 201 Wire Mesh:
Nickel 201 can be hot formed to almost any shape. The temperature range 1200°F to 2250°F is recommended and should be carefully abided as the proper temperature is the most important factor in achieving hot malleability.
Nickel 201 can be cold formed by all conventional methods, but because nickel alloys have greater stiffness than stainless steels more power is required to perform the operations.
|
High Temperature Mechanical Properties of Annealed Nickel 201
|
|
Temp.°F
|
Tensile Strength. PSI
|
Yield Strength. PSI
|
Elongation.%
|
Reduction of Area. %
|
|
Room
|
58.500
|
15.000
|
50
|
73
|
|
200
|
56.100
|
15.400
|
45
|
74
|
|
400
|
54.000
|
14.800
|
44
|
72
|
|
600
|
52.500
|
15.300
|
42
|
72
|
|
800
|
41.200
|
13.500
|
58
|
80
|
|
1000
|
33.100
|
12.100
|
60
|
84
|
|
1200
|
22.200
|
10.200
|
74
|
90
|
Our talented team of experienced wire mesh technicians and engineers employ the latest technologies to produce quality wire mesh and its processed articles.
|
Expanded Mesh
|
|
Perforated Mesh
|
|
Twill Weave mesh
|
|
Dutch Twill Weave Cloth
|
|
Dutch Weave Mesh
|
|
Reverse Dutch Weave Cloth
|
|
5-heddle Weave Mesh
|
|
Cross twill weave
|
|
Plain Weaving Mesh
|
Packing Process & Transportation of Nickel 201 Wire Mesh:
Packaging: Seal up, with plastic inside and wooden case or carton outside; or according to the customer's requirements.
Transportation: By air: Beijing International Airport OR By sea:Trianjin Seaport
We provide our customers with excellent services. If you want more detailed information of this product or related problems, please contact with us, we will reply as soon as possible (general in 24 hours).